All Products

FIBERGLASS- ROLL

Industry Building, HVAC, OEM
Form Rolls
Density 16-48 kg/m3
Thickness 25 mm – 75mm
Packing Polythene-lined hessian bags / Polythene (Shrink wrapped)
Thermal Conductivity 0.030 to 0.041 at 25º C mean temperature
NRC 0.65 to 0.95Conforming to ISO 354
Non-combustibility Non-combustible / Incombustible, Reaction to Fire 'A1' - Confirming to BS 476 Part 4, IS 8183, EN 13501
Facings Unfaced, FSK, WMP, Black Glass Tissue (BGT) , and Alu Glass

FIBERGLASS- BOARD

Industry Building, HVAC, OEM
Form Board
Density 32- 120 kg/m3
Thickness 25mm- 100mm
Packing Polythene-lined hessian bags / Polythene (Shrink wrapped)
Thermal Conductivity 0.030 to 0.034 at 25 º C mean temperature
NRC 0.65 to 0.95Conforming to ISO 354
Non-combustibility Non-combustible / Incombustible, Reaction to Fire 'A1' - Confirming to BS 476 Part 4, IS 8183, EN 13501
Facings Unfaced, FSK, WMP, Black Glass Tissue (BGT) , and Alu Glass

FIBERGLASS-PIPE SECTIONS

Industry HVAC
Form
Density 80 kg/m3
Thickness 25 mm – 75mm
Packing Polythene-lined hessian bags / Polythene (Shrink wrapped)
Thermal Conductivity 0.031 at 25º C mean temperature
NRC 0.65 to 0.95- Conforming to ISO 354
Non-combustibility Non-combustible / Incombustible, Reaction to Fire 'A1' - Confirming to BS 476 Part 4, IS 8183, EN 13501
Facings Unfaced, FSK

FIBERGLASS- ACOUSTIC BOARD

Industry Building, HVAC, OEM
Form Acoustic Board
Density 70 to 80 kg/m3
Thickness 25mm- 50mm
Packing Polythene-lined hessian bags / Polythene (Shrink wrapped)
Thermal Conductivity 0.0306 at 25º C mean temperature
NRC 0.65 with 25 mm thickness
(0.75 with 35 mm air gap)
Non-combustibility Non-combustible / Incombustible, Reaction to Fire 'A1' - Confirming to BS 476 Part 4, IS 8183, EN 13501
Facings FSK on one side + BGC on the other side

ROCKWOOL- LRB MATTRESS

Industry Industry / OEM- Steam pipe, Boiler, Furnace, Tank, Other hot application
Form Low Resin Bonded Mattress
Density 70- 160 kg/m3
Thickness 25- 100mm
Thermal Conductivity 0.059 at 200° C mean temperature
Shot content
 < 25%
Non-combustibility Non-combustible / Incombustible- Confirming to BS 476 Part 4, IS 8183
Facings Unfaced, FSK

ROCKWOOL- RESIN BONDED SLAB

Industry Building, OEM
Form Resin Bonded Slab
Density 40 to 180 kg/m3
Thickness 25 to 150 mm
Thermal Conductivity 0.059 to 0.074 at 200° C mean temperature
Shot Content < 25%
Non-combustibility Non-combustible / Incombustible
Facings FSK, Alu Glass, Black Glass Tissue, and Black Glass Fabric

ROCKWOOL- BUILDING ROLL

Industry Building- Metal building (roof, wall), RCC underdeck, Drywall
Form Building Roll
Density 40 to 100 kg/m3
Thickness 50 to 100 mm
Thermal Conductivity 0.0345 at 25 °C mean temperature
Shot content
 < 25%
Non-combustibility Non-combustible / Incombustible
Facings FSK, Alu Glass

ROCKWOOL- LOOSE WOOL

Industry Industry- Oven, Tile manufacturing, Brake pad, Casting riser, Valves insulation
Form Loose Wool
Density Manually as per requirements
Thickness Manually as per requirements
Thermal Conductivity 0.0595 at 200° C mean temperature
Shot Content < 25%
Non-combustibility Non-combustible / Incombustible
Facings Unfaced and FSK

ROCKWOOL- RESIN BONDED PIPE

Industry OEM
Form Pre- formed Resin Bonded Pipe Section
Density 100 to 160 kg/m3
Thickness 25 to 100 mm
Thermal Conductivity 0.1032 W/mK at 25°C
Shot content
 < 25%
Non-combustibility Non-combustible / Incombustible
Facings Unfaced/ SSK

CERAMIC WOOL

Industry Crude Oil, Reformer & Pyrolysis heater linings, Tube seals, Gaskets & Expansion joints, Heat treatment furnaces
Form Blankets
Density 64-160 kg/m3
Thickness 6mm- 50mm
Thermal Conductivity 0.1032 at 25ºC W/mK
Service Temperature Upto 1425
Non-combustibility Non-combustible / Incombustible, Reaction to Fire 'A1'
Facings Unfaced, Foil-Faced, Vermiculite-Faced, and Needled or Reinforced

POLYURETHANE

Industry HVAC systems, industrial processes, and cold storage
Form PUF Sections (CNC Cut)
Density 36 -50 kg/m3
Thickness 25mm and above
Thermal Conductivity 0.020 to 0.030 W/m·K at 25°C
Service Temperature
-180°C to +120°C
Non-combustibility Fire Resistant
Facings Ceramic fiber blanket
image

POLYISOCYANURATE

Industry Under-deck Roof, Walls, and Flooring of Cold Areas
Form PIC Sections (CNC Cut)
Density 36 -50 kg/m3
Thickness 25mm and above
Thermal Conductivity 0.016 to 0.028 W/mK
Service Temperature -200°C to +140°C
Non-combustibility Non-combustible / Incombustible
Facings Bare, Bituminised Paper, Kraft Paper, Aluminum Foil Paper
image

NITRILE FOAM

Industry Insulation to prevent condensation and reduce energy loss on HVAC ducts, pipes, tanks & equipment.
Form Sheets
Density 40- 60 kg/m3
Confirming to ASTM-D-1065
Thickness 1 mm to 32 mm
Thermal Conductivity ≤0.035 W/m°K at 10°C
≤0.036 W/m°K at 20°C
Service Temperature
-40°C to 105°C
Non-combustibility Class 1 or Class 0 for fire resistance
Facings Unfaced / Alupet / Glass cloth
image

NITRILE FOAM

Industry Insulation to prevent condensation and reduce energy loss on HVAC ducts, pipes, tanks & equipment.
Form Tubing
Density 40- 60 kg/m3
Confirming to ASTM-D-1065
Thickness 6 mm to 32 mm
Thermal Conductivity ≤0.035 W/m°K at 10°C
≤0.036 W/m°K at 20°C
Service Temperature -40°C to 105°C
Non-combustibility Class 1 or Class 0 for fire resistance
Facings Unfaced / Alupet / Glass cloth
image

CELLULAR GLASS

Industry Cold and cryogenic tank bases, • Hot and high temperature tank bases
Form Slab
Density 120 kg/m3
Confirming to EN 1602
Thickness 25mm and above
Thermal Conductivity 0.022 to 0.080 W/(m·K) at -160°C
Service Temperature
-265 to +430 °C
Confirming to EN 14706
Non-combustibility Euroclass A1, Non-combustible
Confirming to EN 13501-1
Compressive Strength CS > 800 kPa
Confirming to EN 826 Annexe A
image

PERLITE

Industry Insulation of Pipes, insulation of reducers, insulation of storage tanks, and insulation of boilers.
Form Slab
Density 192-224 Kg/ Cu.M
Confirmed by ASTM C302/303
Thickness 25 to 100mm
Thermal Conductivity 0.062 W/mK @25°C
Service Temperature
Upto 650° C
Compressive Strength 40 KN/ Sq.M
Confirmed by ASTM C165
Surface burning characteristics
Flame Spread-0 Smoke Developed-5
Confirming to ASTM E84
image

PERLITE

Industry Insulation of Pipes, insulation of reducers, insulation of storage tanks, and insulation of boilers.
Form Sections
Density 192-224 Kg/ Cu.M
Confirmed by ASTM C302/303
Thickness 25 to 100mm
Thermal Conductivity 0.062 W/mK @25°C
Service Temperature Upto 650° C
Compressive Strength 40 KN/ Sq.M
Confirmed by ASTM C165
Surface burning characteristics
Flame Spread-0 Smoke Developed-5
Confirming to ASTM E84
image

POLYURETHANE

Industry Insulation of Pipes, insulation of reducers, insulation of storage tanks, and insulation of boilers.
Form Slabs
Density 30 and 70 kg/m
Thickness 20 to 200mm
Thermal Conductivity 0.025 to 0.035 W/mK at 20°C
Service Temperature
Up to 110°C
Closed Cell Content 85
Compressive Strength 115
Facings Kraft Paper / FSK
image

POLYISOCYANURATE

Industry Insulation of Pipes, insulation of reducers, insulation of storage tanks, and insulation of boilers.
Form Slabs
Density 45 and 70 kg/m³
Thickness 0 to 200mm
Thermal Conductivity 0.022 to 0.027 W/mK at 10°C
Service Temperature Up to 140°C
Closed Cell Content 95
Compressive Strength 115
Facings Kraft Paper / FSK
image

XLPE FOAM

Industry Thermal insulation for pipes, ducts, vessels (including elbows, fittings, flanges, etc)
Form Sheets
Density 30 KG/m³ (Foam core only) (+/-5)
Confirming to ASTM D3575
Thickness 3 to 25mm
Thermal Conductivity 0.031W/mK at 0°C
0.034W/mK at 23°C
Confirming to ASTM C 518
Service Temperature
-20°C to 110°C
Confirming to CIPET
Water vapour diffusion resistance factor ≥ 17000 (Foil Facing)
Confirming to BS EN 12086
image

XLPE FOAM

Industry Thermal insulation for pipes, ducts, vessels (including elbows, fittings, flanges, etc)
Form Tubings
Density 30 KG/m³ (Foam core only) (+/-5)
Confirming to ASTM D3575
Thickness 6, 10, 12, 15, 20, 22, 25, 28, 32, 35, 42, 48, 54, 60mm
Thermal Conductivity 0.031W/mK at 0°C
0.034W/mK at 23°C
Confirming to ASTM C 518
Service Temperature
-20°C to 110°C
Confirming to CIPET
Water vapour diffusion resistance factor ≥ 17000 (Foil Facing)
Confirming to BS EN 12086
image

ALUMINIUM SHEET

Uses Insulation Jacketing (Cladding) on Pipeline & Equipment for all applications
Thickness  18G(1.22mm) , 20G(0.91mm) , 22G(0.71mm) , 24G(0.56mm) , 26G(0.46mm)
Form  Coils  / Corrugated sheets
Finish  Matt
Temper  H14 , H16 & H18 
Alloy  40800, 31500 & 31000 (IS designation)
Mechanical & Chemical Conformance As per  IS 737
image

GALVANISED PLAIN SHEET

Uses Insulation Jacketing (Cladding)  on Grade Pipeline & Equipment 
Thickness  18G(1.25mm) , 20G(1.00mm) , 22G(0.80mm) , 24G(0.60mm) , 26G(0.40mm)
Form  Coils / Sheets
Finish  Matt
Zinc Coating  120, 180 & 275 gsm
Mechanical & Chemical Conformance As per  IS 277
image

ALUMINIZED STEEL SHEET

Uses  Insulation Jacketing (Cladding)  on Pipeline & Equipment required for highly corrosion resistance
Thickness  18G(1.25mm) , 20G(1.00mm) , 22G(0.80mm) , 24G(0.60mm) , 26G(0.40mm)
Form  Sheets / Coils
Finish  Polished
Al-Zinc Coating  100  & 150 gsm
Mechanical & Chemical Conformance As per IS 1608
image

STAINLESS STEEL SHEET

Uses  Insulation Jacketing (Cladding)  on Pipeline & Equipment for highly corrosive areas
Thickness  22G(0.80mm) , 24G(0.60mm) , 26G(0.40mm)
Form  Sheets / Coils
Finish  2B Matt/ Polished
Grade  304 & 316
Mechanical & Chemical Conformance As per IS 228
Uses  Insulation Jacketing (Cladding)  on Pipeline & Equipment
image

HDPE SHEETS

Uses  Transport Containers, Electrical Engineering, Gearwheels and Housing.
Thickness  1 to 200mm
Form  Sheets
DENSITY(BLACK) > 0.950
As per ISO – 1183 / ASTM 1505
MELT FLOW RATE (190°c/5.00 kg) < 0.2-1.4
As per ISO – 1133 / ASTM D 1238
TENSILE STRENGTH @ YIELD ≥ 19
As per ISO – 527 / ASTM D 638 Type-IV
ELONGATION @ BREAK ≥ 350
As per ISO – 527 / ASTM D 638 Type-IV
VICAT SOFTENING TEMPERATURE > 124
As per ASTM D 1525
image

STAINLESS STEEL WIRES

Application  Automotive Products, Braiding Hoses, Brushes, Chains, Conveyor Belts, Filters, Free Cutting Wires, Fasteners, Nails, Flexible Connectors, Kitchen Ware, and Gadgets
Diameter 
 0.43 mm to 1.25 mm 
Grades 
 304 and 316 
Finish Bright, Matte Finish, Soap Coated or Electro Polish Quality
Condition Soft and Solution Annealed
image

GALVANISED WIRES

Application  Commonly used in construction for binding materials, fencing, and reinforcing structures
Diameter 
 0.30 mm to 1.2 mm 
Standards 
 IS: 280- 2006; IS: 398 
Zinc Coating  20 to 60 Gsm/ SqMtr
image

SELF TAPPING SCREW

Material 
 Mild Steel  / Stainless Steel
Thread Type 
 Full Thread 
Size  8 * 13 
Head Type  Pan headed with neoprene washer
image

WING SEAL FOR INSULATION

Application  Strapping on tanks and vessels 
Material 
 Stainless Steel / Aluminum
Seal Thickness 
 0.5 mm to 0.8 mm 
Strap Size  12 mm to 25 mm 
Strap Width 13mm, 15mm, 20mm, 25mm, 40mm, 50mm
image

INSULATION & JACKETING BANDS

Packaging Type
 COIL
Material Grade
 Stainless Steel: 304 
Aluminum: 408000, H14
Thickness 0.4mm up to 1.2mm
Strap Width 13mm, 15mm, 20mm, 25mm, 40mm, 50mm
image

VAPOR BARRIER- MYLAR FOIL

Color Aluminum
As confirmed by TSTM-01 
Composition 0.012 mm Polyester Film 
0.025 mm Aluminum Foil 
0.012 mm Polyester Film
Weight  160 ± 3 % g/m2
Thickness 50 ± 5% ㎛ (polyester film + Al foil)
Water vapour permeance Below 0.005 perms (g/㎡ 24hr) 
Service temperature Temperature at the  coated surface) -
70 ℃ ~ 150 ℃
As confirmed by TSTM-04
Melting point  250 ℃ (polyester)
image

GLASS CLOTH

Color White
As confirmed by TSTM-01 
Composition Glass cloth fabric, leno weave with resin finish
Weight Raw - 58 ± 5 g/㎡
Resin - ≥ 16 g/㎡ 
(resin content - ≥ 18 %)
Warp 34×2 (tex) / 10 (counts/inch)
image

HEAT TRANSFER CEMENT

Color  Black
As confirmed by TSTM-01 
Application Trowel
As confirmed by TSTM-06 
Density 1.65± 0.05 ㎏/ℓ 
As confirmed by ASTM D 1475
Coverage 35.36 ㎏/㎡ (21.43 ℓ/㎡) Dried film thickness: 15 mm 
As confirmed by TSTM-07 
Service temperature limits (Temperature at coated surface) -
100 ℃~ 600 ℃ (-148 ℉ ~ 1112 ℉) 
As confirmed by TSTM-04 
Heat transfer coefficient 100 ~ 200 Kcal/㎡·hr·℃ 
20.48 ~ 40.96 Btu/ft2 ·hr·℉
As confirmed by ASTM C 518
Thermal conductivity  10 ~ 12 Kcal/m·hr·℃ at 200 ℃
As confirmed by ASTM C 518 
image

JACKETING/ CLADDING SEALENT

Color  Aluminum (gray) 
As confirmed by TSTM-01 
Application Caulking gun
As confirmed by TSTM-06 
Density 1.09 ± 0.05 ㎏/ℓ 
As confirmed by ASTM D 147
Coverage Caulking gun (330㎖ tube): - 38m @3.2mm bead 
As confirmed by TSTM-07 
Drying time Set to touch: 30~60 minutes 
Dry through: 72 hours 
As confirmed by ASTM D 1640 
Service temperature limits (Temperature at coated surface) -
101℃ ~ 141℃ (-150℉ ~ 28 
As confirmed by TSTM-04 
Water Vapor permeance  ≤ 0.005 perms (DFT 1.3 mm)
As confirmed by ASTM E 96 
image

INSULATION JOINT SEALENT

Color  Beige (Off-White) 
As confirmed by TSTM-01 
Application Trowel 
As confirmed by TSTM-06 
Density 1.53 ± 0.05 ㎏/ℓ 
As confirmed by ASTM D 1475
Coverage 2.91 ㎏/㎡ (1.90 ℓ/㎡) Dried film thickness: 1.6 mm 
As confirmed by TSTM-07 
Drying time Set to touch: 2 ~ 3 hours. 
Essentially non-drying
As confirmed by ASTM D 1640 
Service temperature limits (Temperature at coated surface) -
196 ℃ ~ 93 ℃ (-321 ℉ ~ 200 ℉) 
As confirmed by TSTM-04 
Water Vapor permeance  ≤ 0.02 perms (DFT 1.3 mm)
As confirmed by ASTM E 96 
image

VAPOR BARRIER- MASTIC

Color  TIC 4055 White / TIC 4056 Gray 
As confirmed by TSTM-01 
Application Trowel or rubber glove 
As confirmed by TSTM-06 
Density 1.20± 0.05 ㎏/ℓ
As confirmed by ASTM D 1475
Coverage 3.43 ~ 5.14 ㎏/㎡ (2.86 ~ 4.28 ℓ/㎡)  
Dried film thickness: 1.2 ~ 1.8 mm
As confirmed by TSTM-07 
Drying time Set to touch: 5 hours 
Dry through: 48 hours
As confirmed by ASTM D 1640 
Service temperature limits (Temperature at coated surface)
-46℃ ~ 121℃ (-51℉ ~ 250℉
As confirmed by TSTM-04 
Water Vapor permeance  ≤ 0.02 perms (DFT 1.3 mm)
image

FIRE RESISTANT ADHESIVE

Color  Beige 
As confirmed by TSTM-01 
Application Trowel
As confirmed by TSTM-06 
Density 1.47 ± 0.05 ㎏/ℓ
As confirmed by ASTM D 1475 
Coverage 2.37 ㎏/㎡ (1.61 ℓ/㎡) 
Dried film thickness: 1.0 mm
As confirmed by TSTM-07 
Bonding time range 10 ~ 20 minutes
As confirmed by TSTM-17 
Service temperature limits  (Temperature at coated surface) -59 ℃ ~ 150 ℃ (-74℉ ~ 302℉)
As confirmed by TSTM-04 
image

JOINT SEALANT

Typical material Foster 95-50 
As per TIC 7020
image

ADHESIVE

Typical material  Foster 81-33 TIC 5080 (one component) 
As per ASTM C871 
image

VAPOR BARRIER

Foil composition: 12 µm polyester film 
25 µm aluminum foil
12 µm polyester film 
Tensile strength   100 MPa
Yield strength 70 N / cm
Tear resistance   400 g / mm
Temperature range  +120°C to -60°C
Water vapour permeability in acc. with ASTM E 96, procedure E (37.8°C, 90% RH)  Max. 10.10-6 g / (m².h.mmHg)